Nickel Alloys

K-500
2.4375

K500 is a quench hardenable nickel-tin alloy. Thanks to titanium and aluminium addition, it gets a good corrosion resistance to seawater, hydrofluoric acid, sulfuric acid and alkaline.

Key benefits

  • Corrosion resistance

  • Low permeability

  • Age hardenable

Normes

  • ASTM B865

  • AMS 4676

Available forms in stock

Diameter
  • from 5 to 300 mm
Thicknesses
  • from 0,4 to 50 mm
Dimensions
  • 1000*2000 mm
Granulometry
  • from 15 microns to 60 microns
Diameter
  • from 10 mm to 50,8 mm
Thickness
  • from 1 mm to 5 mm

Normes

  • ASTM B865

  • AMS 4676

Available forms in stock

Diameter
  • from 5 to 301 mm
Thicknesses
  • from 0,4 mm to 50 mm
Dimensions
  • 1000*2000 mm
Granulometry
  • from 15 microns to 60 microns
Diameter
  • from 10 mm to 50,8 mm
Thickness
  • from 1 mm to 5 mm

Normes

  • ASTM B865

  • AMS 4676

Available forms in stock

Diameter
  • from 5 to 300 mm
Thicknesses
  • from 0,4 to 50 mm
Dimensions
  • 1000*2000 mm
Granulometry
  • from 15 microns to 60 microns
Diameter
  • from 10 mm to 50,8 mm
Thickness
  • from 1 mm to 5 mm

Chemical composition

C
  • 0% min
  • 0,25% max
Mn
  • 0% min
  • 1,5% max
Si
  • 0% min
  • 0,5% max
S
  • 0% min
  • 0,01% max
Ni
  • 63% min
  • 70% max
Cu
  • 27% min
  • 33% max
Ti
  • 0,35% min
  • 0,85% max
Al
  • 2,3% min
  • 3,15% max
Fe
  • 0
  • 2
Back

Mechanical properties

RM (MPA)
1100
RP 0,2 (MPA)
690
Density (G/CM3)
8.44
A (%)
24%