Titanium
Titanium CP
Grade 1
Grade 1 titanium offers the best ductility and formability of the four commercially pure grades, as well as excellent corrosion resistance in oxidising or moderately reducing environments, including chlorides. It has good toughness even at low temperatures and can be easily welded, machined and deformed at hot and cold temperature.
Key benefits
Corrosion resistance
Formability
Weldability
Normes
ASTM F67
ISO 5832-2
Available forms in stock
Diameter
- 0.4 mm to 100 mm
Length
- approx. 3000 mm
Thickness
- 0,4 mm to 60 mm
Dimensions
- Width 1000 to 2000 mm
- Length 1000 to 6000 mm
Diameter
- 0,32 mm to 10 mm
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Thickness
- From 3 mm
Width
- From 10 mm
Length
- Up to 6000 mm
Normes
ASTM B348
ASME SB348
ASTM B265
Available forms in stock
Diameter
- 0.4 mm to 300 mm
Length
- approx. 3000 mm
Thickness
- 0,4 mm to 60 mm
Width
- 1000 to 2000 mm
Length
- 1000 to 6000 mm
Diameter
- 2 mm to 10 mm
Diameter
- 3 to 50,8 mm
Thickness
- 0,3 to 5 mm
Diameter
- 3 to 50,8 mm
Thickness
- 0,3 to 5 mm
Thickness
- from 3 mm
Width
- from 10 mm
Length
- up to 6000 mm
Available forms in stock
Thickness
- From 100 mm
Width
- On demand
Normes
DIN 65039
LN 9297
ASTM B265
WL 3.7024.1
Available forms in stock
Diameter
- 0.4 mm to 300 mm
Length
- approx. 3000 mm
Thickness
- 0,4 mm to 60 mm
Width
- 1000 to 2000 mm
Length
- 1000 to 6000 mm
Diameter
- 0,32 mm to 10 mm
Diameter
- 3 to 50,8 mm
Thickness
- 0,3 to 5 mm
Diameter
- 3 to 50,8 mm
Thickness
- 0,3 to 5 mm
Thickness
- from 3 mm
Width
- from 10 mm
Length
- up to 6000 mm
Chemical composition
Norm of reference : ASTM B348
Fe
- 0% min
- 0,2% max
O
- 0% min
- 0,18% max
N
- 0% min
- 0,03% max
C
- 0% min
- 0,08% max
H
- 0% min
- 0,015% max
Other (each)
- 0% min
- 0,1% max
Other (total)
- 0% min
- 0,4% max
Ti
- —
- Balance
Back
Mechanical properties
Rm (Mpa)
240
Rp 0,2 (Mpa)
170
Density (g/cm3)
4,51
A (%)
25